Materials

FDM / FFF

FDM Nylon 12CF (Carbon Fiber)

Get high stiffness-to-weight ratio with Nylon 12CF. Reinforced with 35% carbon fiber. Experience the highest flexural strength of any FDM 3D printing material.

ABS-M30i

ABS-M30i is a biocompatible thermoplastic 3D printing material perfectly suited for medical, pharmaceutical and food-packaging engineers and designers.

ULTEM™ 1010 resin

ULTEM™ 1010 resin an FDM high-performance thermoplastic. It's strength-to-weight ratio and FST ratings make it an excellent choice for industrial 3D printing.

FDM Nylon 6

The FDM Nylon 6 3D printing material offers the best combination of strength and toughness of any FDM material along with good impact strength.

PC-ABS

The PC-ABS 3D printing material is a high-impact engineering thermoplastic ideal for functional prototyping, tooling and low-volume manufacturing.

ABS-M30 - FDM 3D Printing Material

ABS-M30 an FDM 3D printing material is stronger than standard ABS; ideal for concept modeling, functional prototyping, manufacturing tools and end use parts.

ABS-ESD7

ABS-ESD7 (acrylonitrile butadiene styrene-electrostatic dissipative) thermoplastic with static dissipative properties for static discharge-sensitive applications.

VICTREX AM™ 200 PEEK

High performance PEEK thermoplastic material, semi crystalline, filament for additive manufacturing. For use in higher temperature applications and chemically aggressive environments.

FDM Nylon-CF10

FDM Nylon-CF10 is filled 10% by weight with chopped carbon, which produces a composite material 67% stronger and 190% stiffer than the nylon base material.

FDM Nylon 12

FDM Nylon 12, an FDM 3D printing material is tough, has good impact resistance and high fatigue resistance, making it suitable for snap fit closures.

ST-130

The ST-130 3D printing soluble material is engineered for sacrificial tooling applications for easy creation of hollow composites parts.

PC (Polycarbonate) FDM Filament

Discover the properties and benefits of FDM Polycarbonate 3D printing filament and download the datasheet.

Diran 410MF07

Diran 410MF07 is a durable, nylon-based thermoplastic, demonstrating exceptional toughness and resistance while maintaining a smooth surface quality.

PC-ISO

The PC-ISO 3D printing material is a biocompatible, heat-resistant thermoplastic suitable for food packaging, medical and pharmaceutical applications.

Polyphenylsulfone (PPSU)

The PPSU 3D printing material combines high strength with heat and chemical resistance for demanding
functional testing and production applications.

Antero 800NA

Antero 800NA is a FDM PEKK-based Thermoplastic 3D printing material has excellent mechanical properties chemical resistance and low outgassing characteristics.

FDM HIPS

Discover the properties and benefits of HIPS (high-impact polystyrene) FDM filament and download the datasheet.

Kimya PC-FR

Discover the properties and benefits of Kimya PC-FR flame retardant FDM filament and download the datasheet.

ULTEM™ 9085 Resin

ULTEM™ 9085 resin is a high performance FDM 3D printing material that features a high strength-to- weight ratio; high thermal and chemical resistance.

FDM TPU 92A

FDM TPU 92A 3D printing material provides the flexibility needed to prototype large, complex elastomer parts, with stretch, abrasion, and tear resistance.

Acrylonitrile Styrene Acrylate (ASA)

ASA perfect for 3D printing applications involving prototyping, jigs and fixtures and low-volume production parts. ASA is offered in 10 different color variations.

SLA Materials

Precision Model Resin

Ultimate Tensile Strength: 50.0 MPaTensile Modulus: 2.2 GPaElongation at Break: 8.6%Flexural Strength: 87.0 MPaFlexural Modulus: 2.3 GPaNotched Izod: 32.0 J/mUnnotched Izod: 262.0 J/mHeat Deflection Temp. @ 0.45 MPa: 53.5 °CHeat Deflection Temp. @ 1.8 MPa: 46.0 °CThermal Expansion: 81.1 μm/m/°C

Fast Model Resin

Ultimate Tensile Strength: 62.0 MPaTensile Modulus: 2.67 GPaElongation at Break: 11.0%Flexural Strength: 106.0 MPaFlexural Modulus: 2.74 GPaNotched Izod: 37.0 J/mHeat Deflection Temp. @ 1.8 MPa: 61.0 °CHeat Deflection Temp. @ 0.45 MPa: 76.0 °C

Black Resin V5

Ultimate Tensile Strength: 61.0 MPaTensile Modulus: 2.7 GPaElongation at Break: 10.0%Notched Izod: 29.0 J/mHeat Deflection Temp. @ 0.45 MPa: 69.0Flexural Modulus: 2.75 GPaHeat Deflection Temp. @ 1.8 MPa: 57.0Flexural Strength: 103.0 MPa

White Resin V5

Ultimate Tensile Strength: 61.0 MPaElongation at Break: 11.0%Flexural Strength: 103.0 MPaNotched Izod: 29.0 J/mHeat Deflection Temp. @ 0.45 MPa: 62.0 °CHeat Deflection Temp. @ 1.8 MPa: 54.0 °CTensile Modulus: 2.65 GPaFlexural Modulus: 2.75 GPa

Clear Resin V5

Ultimate Tensile Strength: 60.0 MPaElongation at Break: 8.0%Flexural Strength: 105.0 MPaNotched Izod: 29.0 J/mHeat Deflection Temp. @ 0.45 MPa: 59.0 °CHeat Deflection Temp. @ 1.8 MPa: 74.0 °CTensile Modulus: 2.75 GPaFlexural Modulus: 2.7 GPa

Grey Resin V5

Ultimate Tensile Strength: 62.0 MPaElongation at Break: 13.0%Flexural Strength: 103.0 MPaHeat Deflection Temp. @ 0.45 MPa: 71.0 °CHeat Deflection Temp. @ 1.8 MPa: 59.0 °CNotched Izod: 32.0 J/mTensile Modulus: 2.675 GPaFlexural Modulus: 2.75 GPa

Flame Retardant Resin

Ultimate Tensile Strength: 41.0 MPaTensile Modulus: 3.1 GPaFlexural Strength: 75.0 MPaFlexural Modulus: 2.7 GPaNotched Izod: 22.0 J/mUnnotched Izod: 257.0 J/mElongation at Break: 7.1%Heat Deflection Temp. @ 1.8 MPa: 83.0 °CHeat Deflection Temp. @ 0.45 MPa: 111.0 °CThermal Expansion: 68.1 μm/m/°C

Alumina 4N Resin

Shore Hardness: 70.0 DTensile Modulus: 390.0 GPaFlexural Strength: 400.0 MPa

PU Rigid 1000 Resin

Ultimate Tensile Strength: 35.0 ± 3.5 MPaTensile Modulus: 0.92 ± 0.09 GPaFlexural Strength: 32.0 ± 1.6 MPaFlexural Modulus: 0.75 ± 0.03 GPaNotched Izod: 170.0 J/mElongation at Break: 80.0 ± 8.0%Heat Deflection Temp. @ 1.8 MPa: 64.0 °CHeat Deflection Temp. @ 0.45 MPa: 79.0 °CThermal Expansion: 142.0 μm/m/°C

PU Rigid 650 Resin

Ultimate Tensile Strength: 34.0 ± 3.4 MPaTensile Modulus: 0.67 ± 0.06 GPaFlexural Strength: 22.0 ± 1.1 MPaFlexural Modulus: 0.57 ± 0.03 GPaNotched Izod: 375.0 J/mElongation at Break: 170.0 ± 17.0%Heat Deflection Temp. @ 1.8 MPa: 59.0 °CHeat Deflection Temp. @ 0.45 MPa: 82.0 °CThermal Expansion: 130.4 μm/m/°C

Rigid 10K Resin

Ultimate Tensile Strength: 88.0 MPaTensile Modulus: 11.0 GPaFlexural Strength: 158.0 MPaFlexural Modulus: 9.9 GPaNotched Izod: 20.0 J/mUnnotched Izod: 130.0 J/mElongation at Break: 0.7%Heat Deflection Temp. @ 1.8 MPa: 92.0 °CHeat Deflection Temp. @ 0.45 MPa: 238.0 °CThermal Expansion: 41.0 μm/m/°C

Elastic 50A Resin V2

Ultimate Tensile Strength: 3.4 MPaElongation at Break: 160.0%Shore Hardness: 55.0 ATear Strength: 12.3 kN/mCompression Set 70°C for 22 hours: 3.1%Stress at 100% Elongation: 1.7 MPa

BioMed Flex 80A Resin

Ultimate Tensile Strength: 7.2 MPaStress at 100% Elongation: 4.5 MPaElongation at Break: 135.0%Tear Strength: 22.0 kN/mShore Hardness: 80.0 ACompression Set 70°C for 22 hours: 5.3%

BioMed Elastic 50A Resin

Ultimate Tensile Strength: 2.3 MPaStress at 100% Elongation: 1.3 MPaElongation at Break: 150.0%Tear Strength: 11.0 kN/mShore Hardness: 50.0 ACompression Set 70°C for 22 hours: 11.0%

BioMed Durable Resin

Ultimate Tensile Strength: 29.1 MPaTensile Modulus: 0.994 GPaElongation at Break: 33.0%Flexural Strength: 21.0 MPaFlexural Modulus: 0.643 GPaShore Hardness: 75.0 DNotched Izod: 98.0 J/mUnnotched Izod: 1340.0 J/mHeat Deflection Temp. @ 1.8 MPa: 40.0 °CHeat Deflection Temp. @ 0.45 MPa: 46.0 °C

BioMed Amber Resin

Ultimate Tensile Strength: 73.0 MPaElongation at Break: 12.0%Flexural Strength: 103.0 MPaFlexural Modulus: 2.5 GPaNotched Izod: 28.0 J/mUnnotched Izod: 142.0 J/mHeat Deflection Temp. @ 1.8 MPa: 65.0 °CHeat Deflection Temp. @ 0.45 MPa: 78.0 °C

BioMed Black Resin

Ultimate Tensile Strength: 35.71 MPaTensile Modulus: 1.52374 GPaElongation at Break: 14.0%Flexural Strength: 57.16 MPaFlexural Modulus: 1.66853 GPaShore Hardness: 77.0 DNotched Izod: 24.77 J/mUnnotched Izod: 348.03 J/mHeat Deflection Temp. @ 1.8 MPa: 49.4 °CHeat Deflection Temp. @ 0.45 MPa: 67.9 °C

BioMed White Resin

Ultimate Tensile Strength: 45.78 MPaTensile Modulus: 2.02016 GPaElongation at Break: 10.0%Flexural Strength: 74.46 MPaFlexural Modulus: 2.02016 GPaShore Hardness: 80.0 DNotched Izod: 15.11 J/mUnnotched Izod: 269.03 J/mHeat Deflection Temp. @ 1.8 MPa: 52.4 °CHeat Deflection Temp. @ 0.45 MPa: 67.0 °C

BioMed Clear Resin

Ultimate Tensile Strength: 52.0 MPaElongation at Break: 12.0%Flexural Strength: 84.0 MPaFlexural Modulus: 2.3 GPaShore Hardness: 78.0 DNotched Izod: 35.0 J/mUnnotched Izod: 449.0 J/mHeat Deflection Temp. @ 1.8 MPa: 129.0 °CHeat Deflection Temp. @ 0.45 MPa: 67.0 °CTensile Modulus: 2.08 GPa

IBT Flex Resin

Transparency (2 mm sample): 85.0%Tensile Modulus: 0.008 GPaUltimate Tensile Strength: 7.2 MPaElongation at Break: 135.0%Shore Hardness: 80.0 A

Silicone 40A Resin

Ultimate Tensile Strength: 5.0 MPaElongation at Break: 230.0%Tear Strength: 12.0 kN/mShore Hardness: 40.0 AStress at 100% Elongation: 1.0 MPaRoss Flexing Fatigue: 500000.0 cycles

Castable Wax 40 Resin

ESD Resin

Ultimate Tensile Strength: 44.2 MPaTensile Modulus: 1.937 GPaFlexural Strength: 61.0 MPaFlexural Modulus: 1.841 GPaNotched Izod: 26.0 J/mUnnotched Izod: 277.0 J/mElongation at Break: 12.0%Heat Deflection Temp. @ 1.8 MPa: 54.2 °CHeat Deflection Temp. @ 0.45 MPa: 62.2 °CThermal Expansion: 123.7 μm/m/°C

Castable Wax Resin

Surgical Guide Resin

Elongation at Break: 12.0%Flexural Strength: 102.0 MPaFlexural Modulus: 2.4

Elastic 50A Resin V1

Ultimate Tensile Strength: 3.23 MPaElongation at Break: 160.0%Shore Hardness: 50.0 ATear Strength:
19.1 kN/mCompression Set 70°C for 22 hours: 9.0%Stress at 100% Elongation: 1.59 MPa

Durable Resin

Ultimate Tensile Strength: 28.0 MPaTensile Modulus: 1.0 GPaFlexural Strength: 24.0 MPaFlexural Modulus: 0.66 GPaNotched Izod: 114.0 J/mUnnotched Izod: 710.0 J/mElongation at Break: 55.0%Heat Deflection Temp. @ 0.45 MPa: 41.0 °CThermal Expansion: 106.0 μm/m/°C

Flexible 80A Resin

Ultimate Tensile Strength: 8.9 MPaElongation at Break: 120.0%Shore Hardness: 80.0 ATear Strength: 24.0 kN/mCompression Set 70°C for 22 hours: 5.0%Stress at 100% Elongation: 6.3 MPa

High Temp Resin

Tensile Modulus: 2.8 GPaHeat Deflection Temp. @ 0.45 MPa: 238.0 °CUltimate Tensile Strength: 49.0 MPaFlexural Strength: 97.0 MPaFlexural Modulus: 2.8 GPaNotched Izod: 17.0 J/mElongation at Break: 2.3%Heat Deflection Temp. @ 1.8 MPa: 101.0 °CThermal Expansion: 75.0 μm/m/°C

Rigid 4000 Resin

Ultimate Tensile Strength: 69.0 MPaTensile Modulus: 4.1 GPaFlexural Strength: 105.0 MPaFlexural Modulus: 3.4 GPaNotched Izod: 23.0 J/mElongation at Break: 5.3%Heat Deflection Temp. @ 1.8 MPa: 60.0 °CHeat Deflection Temp. @ 0.45 MPa: 77.0 °CThermal Expansion: 63.0 μm/m/°C

Tough 1500 Resin

Flexural Strength: 39.0 MPaFlexural Modulus: 1.4 GPaNotched Izod: 67.0 J/mUnnotched Izod: 1387.0 J/mElongation at Break: 51.0%Heat Deflection Temp. @ 1.8 MPa: 45.0 °CHeat Deflection Temp. @ 0.45 MPa: 52.0 °CUltimate Tensile Strength: 33.0 MPaTensile Modulus: 1.5 GPaThermal Expansion: 97.0 μm/m/°C

Grey Pro Resin

Ultimate Tensile Strength: 61.0 MPaTensile Modulus: 2.6 GPaFlexural Strength: 86.0 MPaFlexural Modulus: 2.2 GPaNotched Izod: 19.0 J/mElongation at Break: 13.0%Heat Deflection Temp. @ 1.8 MPa: 62.0 °CHeat Deflection Temp. @ 0.45 MPa: 78.0 °CThermal Expansion: 79.0 μm/m/°C

Model V2 Resin

Elongation at Break: 5.0%Ultimate Tensile Strength: 61.0 MPaTensile Modulus: 2.7 GPaFlexural Modulus: 2.5 GPaNotched Izod: 33.0 J/mHeat Deflection Temp. @ 1.8 MPa: 46.0 °CHeat Deflection Temp. @ 0.45 MPa: 49.0 °C

Black Resin V4

Ultimate Tensile Strength: 65.0 MPaTensile Modulus: 2.8 GPaFlexural Modulus: 2.2 GPaNotched Izod: 25.0 J/mElongation at Break: 6.0%Heat Deflection Temp. @ 1.8 MPa: 58.0 °CHeat Deflection Temp. @ 0.45 MPa: 73.0 °C

White Resin V4

Ultimate Tensile Strength: 65.0 MPaTensile Modulus: 2.8 GPaFlexural Modulus: 2.2 GPaNotched Izod: 25.0 J/mElongation at Break: 6.0%Heat Deflection Temp. @ 1.8 MPa: 58.0 °CHeat Deflection Temp. @ 0.45 MPa: 73.0 °C

Tough 2000 Resin

Thermal Expansion: 91.0 μm/m/°CUltimate Tensile Strength: 46.0 MPaTensile Modulus: 2.2 GPaFlexural Strength: 65.0 MPaFlexural Modulus: 1.9 GPaNotched Izod: 40.0 J/mUnnotched Izod: 715.0 J/mElongation at Break: 48.0%Heat Deflection Temp. @ 1.8 MPa: 53.0 °CHeat Deflection Temp. @ 0.45 MPa: 63.0 °C

Model Resin

Ultimate Tensile Strength: 48.0 MPaTensile Modulus: 2.3 GPaElongation at Break: 4.8%Flexural Strength: 85.0 MPaFlexural Modulus: 2.2 GPaNotched Izod: 23.0 J/mUnnotched Izod: 324.0 J/mHeat Deflection Temp. @ 1.8 MPa: 56.0 °CHeat Deflection Temp. @ 0.45 MPa: 75.0 °CThermal Expansion: 76.0 μm/m/°C

Clear Resin V4

Ultimate Tensile Strength: 65.0 MPaTensile Modulus: 2.8 GPaFlexural Modulus: 2.2 GPaNotched Izod: 25.0 J/mElongation at Break: 6.0%Heat Deflection Temp. @ 1.8 MPa: 58.0 °CHeat Deflection Temp. @ 0.45 MPa: 73.0 °C

Draft Resin

Ultimate Tensile Strength: 52.0 MPaTensile Modulus: 2.3 GPaFlexural Modulus: 2.3 GPaNotched Izod: 26.0 J/mElongation at Break: 4.0%Heat Deflection Temp. @ 1.8 MPa: 57.0 °CHeat Deflection Temp. @ 0.45 MPa: 74.0 °CThermal Expansion: 75.0 μm/m/°C

Grey Resin V4

Ultimate Tensile Strength: 65.0 MPaTensile Modulus: 2.8 GPaFlexural Modulus: 2.2 GPaNotched Izod: 25.0 J/mElongation at Break: 6.0%Heat Deflection Temp. @ 1.8 MPa: 58.0 °CHeat Deflection Temp. @ 0.45 MPa: 73.0 °C

Premium Teeth Resin (Form 3)

Flexural Strength: 155.0 MPaFlexural Modulus: 4300.0 MPaShore Hardness: 90.0 D

Denture Teeth Resin 1 L

Flexural Strength: 50.0 MPa

Denture Base Resin 1 L (Form 3)

Flexural Strength: 65.0 MPa

Permanent Crown Resin 1kg (0.7 L)

Flexural Strength: 116.0 MPaFlexural Modulus: 4.09 GPa

Permanent Crown Starter Pack

Temporary CB Resin 1 kg (0.7 L)

Flexural Strength: 100.0 MPa

Dental LT Comfort Resin

Elongation at Break: 33.0%Flexural Strength: 21.0 MPaFlexural Modulus: 0.643 GPaShore Hardness: 75.0 DNotched Izod: 98.0 J/m

Dental LT Clear V2 Resin

Ultimate Tensile Strength: 52.0 MPaTensile Modulus: 2.08 GPaElongation at Break: 12.0%Flexural Strength: 84.0 MPaFlexural Modulus: 2.3 GPaShore Hardness: 78.0 D